双相超高强度时效不锈钢
无权-届满

TWO-PHASE SUPER-STRENGTH AGED STAINLESS STEEL

申请号:85106667 申请日:1985-09-06
摘要:本发明系双相超高强度时效不锈钢,是一种 Cr-Ni-Mo-Al系马氏体-铁素体型(约50%马 氏体+50%铁素体)时效不锈钢。该钢采用真空感 应或真空+电渣冶炼后,经820~1040℃的固溶处 理和500~600℃的时效处理,强度可达150公斤/毫 米2,且具有较高的塑性和优异的抗腐蚀性能以及良 好的尺寸稳定性。本发明还具有工艺简单、热加工性 能好和易于机械加工等特点。
Abstract: The invention concerns a two-phase super-strength aged stainless steel, belonging to the martensite-ferrite aged stainless steel (about 50% martensite and 50% ferrite). By vacuum induction smelting or vaccum plus electroslag smelting, then by solid solution treatment at 820-1040 deg.C. and aging treatment at 500-600 deg.C., the steel may have a strength of 150kg/squared mm, as well as high plasticity, excellent corrosion resistant properties and good dimensional stability. The invention also has the advantages of simple in technol, and giving a product of good thermal treatment performance and easy to be machined.
申请人: 冶金工业部钢铁研究总院 抚顺钢厂
Applicant:
地址: 北京市学院南路24********(隐藏)
发明(设计)人: 赵瑛伟 刘连仲
Inventor:
主分类号: C22C38/44
分类号: C22C38/44
  • 法律状态
1987-04-22  授权
1986-10-22  审定
1986-10-22  公开
1986-01-10  
注:本法律状态信息仅供参考,即时准确的法律状态信息须到国家知识产权局办理专利登记簿副本。
  • 其他信息
主权项  1、一种超高强度双相时效不锈钢,其特征在于钢的组织结构由马氏体和铁素体组成,具体化学成分为: C<0.03%、14.0~17.0%Cr、5.0~7.0%Ni、3.1~3.8%Mo、1.2~1.5%Al,或另加0.3~0.6%Re。
公开号  85106667A
公开日  1986-10-22
专利代理机构  中国法律事务公司
代理人  成光祜
颁证日  
优先权  
 
国别 优先权号 优先权日 类型
CN  85106667  19850906 
国际申请  
国际公布  
进入国家日期  
  • 专利对比文献
类型 阶段 文献号 公开日期 涉及权利要求项 相关页数
注:不保证该信息的有效性、完整性、准确性,以上信息也不具有任何效力,仅供参考。使用前请另行委托专业机构进一步查核,使用该信息的一切后果由用户自行负责。
X:单独影响权利要求的新颖性或创造性的文件;
Y:与检索报告中其他 Y类文件组合后影响权利要求的创造性的文件;
A:背景技术文件,即反映权利要求的部分技术特征或者有关的现有技术的文件;
R:任何单位或个人在申请日向专利局提交的、属于同样的发明创造的专利或专利申请文件;
P:中间文件,其公开日在申请的申请日与所要求的优先权日之间的文件,或会导致需核实该申请优先权的文件;
E:单独影响权利要求新颖性的抵触申请文件。
  • 期刊对比文献
类型 阶段 期刊文摘名称 作者 标题 涉及权利要求项 相关页数
  • 书籍对比文献
类型 阶段 书名 作者 标题 涉及权利要求项 相关页数
  • 附加信息
同族专利
CN85106667B
 
引用文献
 
被引用文献
CN101701555ACN103801646ACN108237209A
CN1330785C