一种磨钢球砂轮结合剂及其生产方法
无权-视为撤回

Steel ball grinding abrasive wheel binder and its production method

申请号:03152824.4 申请日:2003-08-20
摘要:本发明属于磨钢球砂轮结合剂技术领域,其有效化学成分(重量百分比)为:氧化硅56.1%~60.3%,氧化铝23.5%~26.7%,氧化铁<1.0%,氧化钙<0.5%,氧化钾+氧化钠7.0%~9.0%,氧化硼1.46%~2.20%,氧化锰3.25%~5.2%。本发明还提供了一种生产结合剂的方法:分别称取粘土、长石、硼玻璃、金属氧化物,混合,粉碎,通过240目筛网过筛。本发明由于加入金属氧化物,特别是氧化锰,使结合剂耐热性高,耐磨性好,可提高产品合格率16~18%,降低能耗30%~36%。
Abstract: The present invention belongs to the field of ball-grinding abrasive-disk anchoring agent technology. Its effective chemical components are: (wt%) silicon oxide 56.1%-60.3%, aluminium oxide 23.5%-26.7%, iron oxide less than 1.0%, calcium oxide less than 0.5%, potassium oxide+sodium oxide 7.0%-9.0%, boron oxide, 1.46%-2.20% and manganese oxide 3.25%-5.2%. The production method of said anchoring agent includes the following steps: respectively weighing clay, feldspar, boron glass and metal oxide, mixing them, pulverizing and sieving by means of 240-mesh sieve. The anchoring agent has high heat resistance and wear resistance.
申请人: 扬州市东方砂轮厂
Applicant: DONGFANG GRINDING WHEEL FACTOR[CN]
地址: 225238江苏省********(隐藏)
发明(设计)人: 丁辛喜
Inventor: DING XINXI[CN]
主分类号: B24D3/06
分类号: B24D3/06
  • 法律状态
2007-04-25  
2004-07-28  公开
注:本法律状态信息仅供参考,即时准确的法律状态信息须到国家知识产权局办理专利登记簿副本。
  • 其他信息
主权项  1、一种磨钢球砂轮的结合剂,其特征在于其有效化学成份(重量百分比) 为:氧化硅56.1%~60.3%,氧化铝23.5%~26.7%,氧化铁<1.0%,氧化钙 <0.5%,氧化钾+氧化钠7.0%~9.0%,氧化硼1.46%~2.20%,氧化锰3.25%~ 5.2%。
公开号  1515383A
公开日  2004-07-28
专利代理机构  扬州市锦江专利事务所
代理人  秦关华
颁证日  
优先权  
 
国别 优先权号 优先权日 类型
CN  03152824  20030820 
国际申请  
国际公布  
进入国家日期  
  • 专利对比文献
类型 阶段 文献号 公开日期 涉及权利要求项 相关页数
注:不保证该信息的有效性、完整性、准确性,以上信息也不具有任何效力,仅供参考。使用前请另行委托专业机构进一步查核,使用该信息的一切后果由用户自行负责。
X:单独影响权利要求的新颖性或创造性的文件;
Y:与检索报告中其他 Y类文件组合后影响权利要求的创造性的文件;
A:背景技术文件,即反映权利要求的部分技术特征或者有关的现有技术的文件;
R:任何单位或个人在申请日向专利局提交的、属于同样的发明创造的专利或专利申请文件;
P:中间文件,其公开日在申请的申请日与所要求的优先权日之间的文件,或会导致需核实该申请优先权的文件;
E:单独影响权利要求新颖性的抵触申请文件。
  • 期刊对比文献
类型 阶段 期刊文摘名称 作者 标题 涉及权利要求项 相关页数
  • 书籍对比文献
类型 阶段 书名 作者 标题 涉及权利要求项 相关页数